Taşaltın, NevinTaşaltın, CihatKarakuş, SelcanBaytemir, Gülsen2024-07-122024-07-122022Taşaltın, N., Taşaltın, C., Karakuş, S. and Baytemir, G. (2022). Energy storage performance of three-dimensional ta nanopillars based electrode for supercapacitors. Journal of Energy Storage. 51, s.1-4.2352-153810.1016/j.est.2022.1044742-s2.0-85127222680https://doi.prg/10.1016/j.est.2022.104474https://hdl.handle.net/20.500.12415/3207In this study, Ta nanopillar array was prepared using Anodic aluminium oxide (AAO) nanotemplate assisted method. Ta nanopillars are approximately 80 nm in width and 150 nm in length. In electrochemical measurements, the electrons in the Ta nanopillars and ions in the H2SO4 electrolyte formed the electrical double layer supercapacitor (EDLC). The specific capacitance of the Ta nanopillar array electrode was 640 Fg -1. Ta nanopillararray electrode has 86% retention after 1000 cycles. The results reveal that the Ta nanopillar array-based electrode is a potential candidate electrode material for supercapacitors.Bu çalışmada, Anodik alüminyum oksit (AAO) nanoşablon destekli yöntem kullanılarak Ta nanopillar dizisi hazırlandı. Ta nanosütunları yaklaşık 80 nm genişliğinde ve 150 nm uzunluğundadır. Elektrokimyasal ölçümlerde Ta nanosütunlarındaki elektronlar ve H2SO4 elektrolitindeki iyonlar elektriksel çift katmanlı süper kapasitörü (EDLC) oluşturdu. Ta nanopillar dizisi elektrotunun spesifik kapasitansı 640 Fg-1 idi. Ta nanopillararray elektrotu 1000 döngüden sonra %86 tutma oranına sahiptir. Sonuçlar, Ta nanopillar dizi bazlı elektrotun süper kapasitörler için potansiyel bir aday elektrot malzemesi olduğunu ortaya koyuyor.eninfo:eu-repo/semantics/openAccessEnergy storageSupercapacitorNanopillarInterfacesEnerji depolamaSüper kapasitörNano sütunArayüzlerArticle4N/A151WOS:000793718800003Q1