Mechanical properties of magnesium phosphate cement incorporating basalt fibers

Küçük Resim Yok

Tarih

2021

Dergi Başlığı

Dergi ISSN

Cilt Başlığı

Yayıncı

Stowarzyszenie Producentow Cementu

Erişim Hakkı

info:eu-repo/semantics/openAccess

Araştırma projeleri

Organizasyon Birimleri

Dergi sayısı

Özet

In this experimental study, the effect of basalt fibers on the mechanical properties of magnesium phosphate cement [MPC] was investigated. Compressive strength, splitting tensile strength, flexural strength and modulus of elasticity, were introduced. It was observed that mechanical properties were significantly enhanced with the addition of silica fume, especially splitting tensile and flexural strength were enhanced with the increase of basalt fibers. However, for mixtures without silica fume addition, high content of fibers adversely affected the mechanical properties. Silica fume addition was found to be significant in increasing the bonding mechanism between basalt fibers and the MPC matrix. Thus, combined usage of silica fume and basalt fibers was found to be effective. A molar ratio of magnesia to ammonium dihydrogen phosphate of 8 was observed to have better results with respect to a molar ratio of 6, however, this distinction was not very apparent, when silica fume was added to both mixtures.

Açıklama

Anahtar Kelimeler

Magnesium Phosphate Cement, Silica Fume, Basalt Fibers, Modulus Of Elasticity

Kaynak

Cement Wapno Beton

WoS Q Değeri

Q4

Scopus Q Değeri

Q3

Cilt

26

Sayı

3

Künye